Rubinsztajn, Slawomir (Niskayuna, NY, US)

Plaque It!

11/165093

11/04/2008

06/23/2005

Images are available in PDF form when logged in. To view PDFs, Login  or  Create Account (Free!)

Click for automatic bibliography generation

Momentive Performance Materials Inc. (Albany, NY, US)

523/216

523/200, 524/261, 428/356EP, 523/443, 524/80, 428/413, 524/266, 523/457, 523/427, 428/402, 523/445, 523/456, 523/440, 428/355R, 523/466, 524/81

C08K9/02; C08K9/00; B32B27/04; B32B27/38

524/261, 523/216, 523/200, 524/80, 523/443, 428/405, 524/266, 428/407, 428/413, 523/457, 523/427, 428/402, 523/445, 428/403, 523/456, 523/440, 428/355R, 523/466, 428/404, 524/81, 428/355EP

3338871	Process for preparing polyepoxide compositions	August, 1967	Vogelz
3479317	ADHESIVE ADDITIVES FOR CURABLE LIQUID RESINS	November, 1969	Ferington
3666695	AN EPOXY RESIN ADHESIVE CONTAINING A POLYMERIC FATTY-AMIDO AMINE AND MONOMERIC FATTY-AMIDO AMINE MIXTURE AS THE CURING AGENT	May, 1972	Jachimowicz et al.
3864426	Thermal shock resistant epoxy compositions	February, 1975	Salensky
3956214	Method of preparing curable pellets of polyethylene with a motionless mixer	May, 1976	Tate et al.
4026862	Carboxylic acid storage stabilizers for latent catalyst cured epoxy resins	May, 1977	Smith et al.
4042550	Encapsulant compositions based on anhydride-hardened epoxy resins	August, 1977	Tuller et al.
4066625	Unitary curable resin compositions	January, 1978	Bolger
4178274	Casting resin compositions for sealing opto-electronic components	December, 1979	Denk et al.
4217438	Polycarbonate transesterification process	August, 1980	Brunelle et al.
4331582	Epoxy latent catalyst	May, 1982	Babayan
4336367	Epoxy adhesive composition	June, 1982	Morris et al.
4496687	Aqueous emulsion-type silicone compositions	January, 1985	Okada et al.
4521490	Two-part epoxy composition	June, 1985	Pocius et al.
4684678	Epoxy resin curing agent, process, and composition	August, 1987	Schultz et al.
4692272	Thermally stable adhesive comprising soluble polyimide resin and epoxy resin	September, 1987	Goswami et al.
4869772	Diazabicyclo and triazabicyclo primer compositions and use thereof in bonding non-polar substrates	September, 1989	McDonnell et al.
4999699	Solder interconnection structure and process for making	March, 1991	Christie et al.
5121190	Solder interconnection structure on organic substrates	June, 1992	Hsiao et al.
5128746	Adhesive and encapsulant material with fluxing properties	July, 1992	Pennisi et al.
5145889	Acid anhydride-cured epoxy resin encapsulant with triorganothiophosphite	September, 1992	Wada et al.
5194930	Dielectric composition and solder interconnection structure for its use	March, 1993	Papathomas et al.
5212261	Latent, heat-curable epoxy resin compositions containing metal carboxylate curing systems	May, 1993	Stierman
5376403	Electrically conductive compositions and methods for the preparation and use thereof	December, 1994	Capote
5417771	Soldering flux	May, 1995	Arita et al.
5471027	Method for forming chip carrier with a single protective encapsulant	November, 1995	Call et al.
5580655	Silica nanoparticles	December, 1996	El-Shall et al.
5616633	Liquid epoxy resin composition	April, 1997	Wombwell et al.
5644003	Epoxy resin composition, process for producing the same and resin-sealed semiconductor device	July, 1997	Arai et al.
5700581	Solvent-free epoxy based adhesives for semiconductor chip attachment and process	December, 1997	Sachdev et al.
5821456	Microelectronic assembly including a decomposable encapsulant, and method for forming and reworking same	October, 1998	Wille et al.
5985043	Polymerizable fluxing agents and fluxing adhesive compositions therefrom	November, 1999	Zhou et al.
6010577	Multifunctional soldering flux with borneol	January, 2000	Bristol et al.
6017634	Carboxyl-containing polyunsaturated fluxing agent and carboxyl-reactive neutralizing agent as adhesive	January, 2000	Capote et al.
6059894	High temperature flip chip joining flux that obviates the cleaning process	May, 2000	Pendse
6103379	Process for the preparation of microspheres and microspheres made thereby	August, 2000	Margel et al.
6132646	Polmerizable fluxing agents and fluxing adhesive compositions therefrom	October, 2000	Zhou et al.
6180696	No-flow underfill of epoxy resin, anhydride, fluxing agent and surfactant	January, 2001	Wong et al.	523/457
6194788	Flip chip with integrated flux and underfill	February, 2001	Gilleo et al.
6210811	Epoxy resin composition, laminate film using the same, and semiconductor device	April, 2001	Honda et al.
6232264	Polymetallic precursors and compositions and methods for making supported polymetallic nanocomposites	May, 2001	Lukehart et al.
6235865	Phosphonium borate compound, making method, curing catalyst, and epoxy resin composition	May, 2001	Shimizu et al.
6372839	Flip-chip type semiconductor device underfill	April, 2002	Ito et al.
6379799	Low moisture absorption epoxy resin systems with alkylated diamine hardeners	April, 2002	Almen
6380322	Reworkable high temperature adhesives	April, 2002	Wong et al.
6437026	Hardener for epoxy molding compounds	August, 2002	Garrett
6444495	Dielectric films for narrow gap-fill applications	September, 2002	Leung et al.
6458472	Fluxing underfill compositions	October, 2002	Konarski et al.
6467676	Fluxing adhesive	October, 2002	Wang
6486235	Composition of epoxy resin, curing agent, phosphate of resorcinol, Al (OH)	November, 2002	Cooray et al.
6492438	Electrically connectable adhesive agent for semiconductor	December, 2002	Nomura
6500544	Corrosion resistant coatings	December, 2002	Tiitu et al.
6531704	Nanotechnology for engineering the performance of substances	March, 2003	Yadav et al.
6548189	Epoxy adhesive	April, 2003	Gunasekaran et al.
6554609	Nanotechnology for electrical devices	April, 2003	Yadav et al.
6555602	Composition of epoxy resin, anhydride and microcapsule accelerator	April, 2003	Harada et al.
6570029	No-flow reworkable epoxy underfills for flip-chip applications	May, 2003	Wand et al.
6576355	Nanotechnology for electronic and opto-electronic devices	June, 2003	Yadav et al.
6576718	Powder coating of thermosetting resin(s) and poly(phenylene ethers(s))	June, 2003	Yeager et al.
6607821	Applications and devices based on nanostructured non-stoichiometric substances	August, 2003	Yadav et al.
6617400	Composition of cycloaliphatic epoxy resin, anhydride curing agent and boron catalyst	September, 2003	Yeager et al.
6617401	Composition comprising cycloaliphatic epoxy resin, 4-methylhexahydrophthalic anhydride curing agent and boron catalyst	September, 2003	Rubinsztajn
6620512	Anhydride polymers for use as curing agents in epoxy resin-based underfill material	September, 2003	Jayaraman et al.	428/414
6624213	High temperature epoxy adhesive films	September, 2003	George et al.
6624216	No-flow underfill encapsulant	September, 2003	Morganelli et al.
6689469	Crystalline polymer nano-particles	February, 2004	Wang et al.
6706417	Fluxing underfill compositions	March, 2004	Konarski et al.
6710011	Catalyst compositions for the ammoxidation of alkanes and olefins, methods of making and of using same	March, 2004	Mamedov et al.
6773958	Integrated assembly-underfill flip chip process	August, 2004	Wang
6794761	No-flow underfill material	September, 2004	Shi et al.
6809162	Solid state device with encapsulant of cycloaliphatic epoxy resin, 4-methylhexahydrophthalic anhydride and boron catalyst	October, 2004	Rubinsztajn
6822341	Latent catalysts for molding compounds	November, 2004	Ahsan
6830822	Inorganic colors and related nanotechnology	December, 2004	Yadav
6849109	Inorganic dopants, inks and related nanotechnology	February, 2005	Yadav et al.
6866741	Method for joining large substrates	March, 2005	Chan
7022410	Combinations of resin compositions and methods of use thereof	April, 2006	Tonapi
7041736	Anhydride polymers for use as curing agents in epoxy resin-based underfill material	May, 2006	Jayaraman et al.	525/117
7202304	Anhydride polymers for use as curing agents in epoxy resin-based underfill material	April, 2007	Jayaraman et al.	525/117
20020137260	DIELECTRIC FILMS FOR NARROW GAP-FILL APPLICATIONS	September, 2002	Leung et al.
20030004268	Polyimide blends, method of making, and articles made therefrom	January, 2003	Sundararaj et al.
20030071368	Epoxy resin compositions, solid state devices encapsulated therewith and method	April, 2003	Rubinsztajn
20030124353	Crystalline polymer nano-particles	July, 2003	Wang et al.
20030198810	Nano-particle preparation and applications	October, 2003	Wang et al.
20030218258	Nanoparticle filled underfill	November, 2003	Charles et al.
20040101688	Curable epoxy compositions, methods and articles made therefrom	May, 2004	Rubinsztajn
20040102529	Functionalized colloidal silica, dispersions and methods made thereby	May, 2004	Campbell
20040159328	Use of oxyhydroxide compounds for reducing carbon monoxide in the mainstream smoke of a cigarette	August, 2004	Hajaligol et al.
20040180203	Nanomaterial compositions with distinctive shape and morphology	September, 2004	Yadav et al.
20040192947	Mesostructured catalyst incorporating particles of nanometric dimensions	September, 2004	Chane-Ching et al.
20040228967	Dielectric films for narrow gap-fill applications	November, 2004	Leung et al.
20050048291	Nano-filled composite materials with exceptionally high glass transition temperature	March, 2005	Woo et al.
20050049334	Solvent-modified resin system containing filler that has high Tg, transparency and good reliability in wafer level underfill applications	March, 2005	Rubinsztajn
20050049350	Thin bond-line silicone adhesive composition and method for preparing the same	March, 2005	Tonapi et al.
20050049352	Solvent-modified resin compositions and methods of use thereof	March, 2005	Rubinsztajn
20050049357	Thin bond-line silicone adhesive	March, 2005	Zhong et al.
20050065023	Nanocomposite copper-ceria catalysts for low temperature or near-ambient temperature catalysis and methods for making such catalysts	March, 2005	Deevi et al.
20050113489	Solution containing surface-modified nanoparticles	May, 2005	Baran et al.
20050131106	Combinations of resin compositions and methods of use thereof	June, 2005	Tonapi et al.
20050170188	Resin compositions and methods of use thereof	August, 2005	Campbell et al.	428/413
20050266263	Refractory solid, adhesive composition, and device, and associated method	December, 2005	Campbell et al.	428/624
20060125119	B-stageable underfill encapsulant and method for its application	June, 2006	Xiao et al.	257/793
20060147719	Curable composition, underfill, and method	July, 2006	Rubinsztajn et al.	428/413
20060219757	Method for producing cure system, adhesive system, and electronic device	October, 2006	Rubinsztajn

CA1094706	January, 1981
WO/1991/006594	May, 1991			POLYMERIC COMPOSITIONS

International Search Report dated Aug. 3, 2006.
U.S. Appl. No. 11/155,990, filed Jun. 2005, Campbell.
U.S. Appl. No. 10/654,378, filed Sep. 2003, Rubinsztajn.
U.S. Appl. No. 10/737,943, filed Dec. 2003, Rubinsztajn.
U.S. Appl. No. 11/096,160, filed Apr. 2005, Campbell.

Mcclendon, Sanza L.

Vicari, Dominick G.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims benefit and priority to U.S. Provisional patent application Ser. No. 60/668,651, filed Apr. 5, 2005. The entire contents of which are hereby incorporated by reference.

What is claimed is:

1. A method of producing a cure system, comprising: mixing a curing agent that is a low temperature liquid and a finely divided refractory solid, wherein the solid has an active termination site density that is less than about 5 per square nanometer and, wherein the refractory solid is non-reactive with the curing agent.

2. The method as defined in claim 1, wherein the refractory solid is compatiblized and passivated.

3. The method as defined in claim 2, wherein the curing agent comprises an anhydride.

4. The method as defined in claim 3, wherein the anhydride comprises one or more aromatic carboxylic acid anhydride, aliphatic carboxylic acid anhydride, cycloaliphatic carboxylic acid anhydride, or siloxane dianhydride.

5. The method as defined in claim 3, wherein the anhydride comprises one or more of benzoic anhydride; phthalic anhydride; hexahydro phthalic anhydride; methyl-hexahydro phthalic anhydride (MHHPA); 4-nitrophthalic anhydride; naphthalene tetracarboxylic acid dianhydride; naphthalic anhydride; tetrahydro phthalic anhydride; cyclohexane dicarboxylic anhydride; butanoic anhydride; dodecenyl succinic anhydride; 2,2-dimethyl glutaric anhydride; ethanoic anhydride; glutaric anhydride; hexafluoro glutaric acid anhydride; itaconic anhydride; tetrapropenylsuccinic anhydride; maleic anhydride; 2-methyl glutaric anhydride; 2-methyl propionic anhydride 1,2-cyclohexane dicarboxylic anhydride; octadecyl succinic anhydride; 2-octenyl succinic anhydride; n-octenyl succinic anhydride; 2-phenyiglutaric anhydride; propionic acid anhydride; 3,3-tetramethylene glutaric anhydride; or derivatives thereof.

6. The method as defined in claim 1, wherein the curing agent is a liquid at a temperature in a range of less that about 100 degrees Celsius.

7. The method as defined in claim 6, wherein the curing agent is a liquid at a temperature in a range of less that about 50 degrees Celsius.

8. The method as defined in claim 7, wherein the curing agent is a liquid at a temperature in a range of from about 25 degrees Celsius to about 35 degrees Celsius.

9. The method as defined in claim 1, wherein the refractory solid comprises silica.

10. The method as defined in claim 9, wherein the silica comprises silica particles.

11. The method as defined in claim 9, wherein the silica particles have an average particle size that is nano-scale.

12. The method as defined in claim 11, wherein the silica particles have an average particle size that is in a range of less than about 100 nanometers.

13. The method as defined in claim 1, further comprising admixing a catalyst or an accelerator into the mixture of curing agent and solid.

14. The method as defined in claim 1, further comprising admixing one or more of pigment, reactive diluent, suspension agent, defoamer, flow modifier, flexibilizer, or flame retardant into the mixture of curing agent and solid.

15. The method as defined in claim 1, further comprising admixing an adhesion promoter into the mixture of curing agent and solid.

16. The method as defined in claim 2, wherein the refractory solid comprises one or both of alumina or boron nitride.

17. The method as defined in claim 1, wherein the refractory solid is present in an amount in a range of from about 30 weight percent to about 70 weight percent based on the total weight of the composition.

18. A cure system produced by the method as defined in claim 1.

19. An adhesive system comprising a curable resin and the cure system as defined in claim 18.

20. The adhesive system as defined in claim 19, wherein the curable resin comprises one or more epoxy or oxirane moiety.

21. The adhesive system as defined in claim 19, wherein the adhesive system has a viscosity at about room temperature that is sufficiently low to enable application of the adhesive system to a substrate surface and to be used as a no-flow underfill.

22. A cured polymer layer comprising the adhesive system as defined in claim 19.

23. A method, comprising: dispersing a compatibilized and passivated refractory solid into a mixture or solution of a low temperature liquid curing agent and a low boiling solvent, wherein the solvent is free of hydroxyl-groups and the curing agent does not react with the solid and wherein the solid has an active termination site density that is less than about 5 per square nanometer; and removing the solvent from the mixture or solution to form a solvent-free liquid dispersion of curing agent and refractory solid.

24. The method as defined in claim 23, further comprising mixing the dispersion with a curable resin to form an adhesive system.

25. The method as defined in claim 24, further comprising applying a portion of the adhesive system to a substrate and contacting the portion with an electronic component, and curing the adhesive system to secure the chip to the substrate.

26. A system, comprising: means for securing a chip to a substrate; means for curing the securing means and wherein the securing means is the cured polymer layer of claim 22; and means for matching the coefficient of thermal expansion of the securing means to one or both of the chip or substrate, wherein the matching means is dispersed in the curing means.

BACKGROUND

The invention includes embodiments that relate to a method for producing a cure system and for an adhesive system. The invention includes embodiments that relate to a method for producing an electronic device.

Semiconductor chips may be mounted to a substrate in an electronic device. The mounting may not be perfect and air-filled gaps may result between a surface of the chip and a surface of the mounting substrate. Because the air gaps may be undesirable, an underfill resin may be used to fill in the gaps. Underfill material may be used to improve reliability of the device. Further, the use of an underfill material may improve a fatigue life of solder bumps in an assembly.

To address shortcomings associated with traditional capillary underfill resins, a No-Flow Underfill (NFU) material was developed. No-Flow Underfill may include a curable resin, such as an epoxy resin, and may be unfilled, or filled with nano-size filler. The resin filler may be functionalized colloidal silica. The higher the filler content in the resin, the closer may be a match of the coefficient of thermal expansion (CTE) of the cured resin relative to a semiconductor chip. Unfortunately, for reasons of processability and the like, filler loadings of more than about 50 weight percent in the uncured resin may be problematic. To exacerbate the situation, after the addition of a curing agent, the final filler loading may be below 30 weight percent of the total composition. A typical CTE of a cured no-flow underfill epoxy resin with filler loading below 30 weight percent may be above 50 ppm/° C.

It may be desirable to have an underfill material having one or more of a coefficient of thermal expansion of less than 50 ppm/° C., a filler loading of greater than 30 weight percent, an acceptable level of processability, transparency, or a desirably high glass transition temperature (Tg). It may be desirable to have a process for making and/or using an underfill material system having improved or different properties than are currently available. It may be desirable to have an apparatus or article employing a no-flow underfill material system having improved or different properties than are currently available.

BRIEF DESCRIPTION

An embodiment of the invention may provide a method of producing a cure system. The method may include mixing a curing agent that is a low temperature liquid and a finely divided refractory solid. The refractory solid may be non-reactive with the curing agent.

An embodiment of the invention may provide a method, including dispersing a compatibilized and passivated refractory solid into a mixture or solution of a low temperature liquid curing agent and a low boiling solvent, and removing the solvent from the mixture or solution to form a solvent-free liquid dispersion of curing agent and refractory solid. The solvent may be free of hydroxyl-groups and the curing agent may not react with the solid.

In one aspect, the method may further include mixing the dispersion with a curable resin to form an adhesive system. In another aspect, the method may further include applying a portion of the adhesive system to a substrate and contacting the portion with an electronic component. The adhesive system may be cured to secure the chip to the substrate.

In one embodiment, the invention may provide a system, including means for securing a chip to a substrate, means for curing the securing means; and means for matching the coefficient of thermal expansion of the securing means to one or both of the chip or substrate. The matching means may be dispersed in the curing means.

DETAILED DESCRIPTION

The invention includes embodiments that relate to a cure system comprising a compatiblized and passivated refectory solid and a hardener or a curing agent (collectively “curing agent”). The curing agent may be liquid or fluid at a low temperature. The invention includes embodiments that relate to methods of making and/or using the cure system. In one embodiment, an adhesive system includes the cure system in combination with a curable resin. Other embodiments relate to electronic devices made using the adhesive system.

As used herein, cured refers to a curable composition having reactive groups in which more than half of the reactive groups have reacted or cross linked; curing agent refers to a material that may interact with a curable resin to crosslink monomers in a resin system, such as an epoxy resin. Approximating language, as used herein throughout the specification and claims, may be applied to modify any quantitative representation that could permissibly vary without resulting in a change in the basic function to which it is related. Accordingly, a value modified by a term or terms, such as “about”, may not to be limited to the precise value specified. In at least some instances, the approximating language may correspond to the precision of an instrument for measuring the value.

Hydroxyl-free, hydroxyl-group free, solvent-free, no-flow, and the like include a complete absence of the indicated material or property, and further include a substantial absence of the indicated material. That is, the “no-” and “-free” modifiers, and the like, are not used in a strict or absolute sense and may contain insignificant, trace, residual or minimal amounts of the indicated material or property unless context or language indicates otherwise. Derivatives may include conjugate acids or salts. Stability, as used herein in the specification and claims, refers to the lack of reaction, or the lack thereof, of active termination sites on the surface of the refractory solid and the curing agent over a period of time, e.g., one week, two weeks, and the like. The term “functionalized” may refer to a material in which functional groups have been manipulated or affected in some manner, such as reacted with a compatibilizing material or a passivating material.

In one embodiment, a room temperature liquid cure system may include a compatiblized and passivated refectory solid and a liquid curing agent. The cure system may be combined with a curable resin to initiate cure of the resin, that is, to crosslink reactive monomers contained in the resin. Particularly, the compatiblized and passivated refectory solid may be homogeneously dispersed into a low temperature liquid curing agent as filler to form the cure system. In one embodiment, the cure system may be combined with a curable resin to form an adhesive system. The adhesive system may cure quickly after combining, may have a pot life that extends for hours or days, or may have an indefinite pot life or desirable shelf life until a further triggering event occurs, such as the application of energy to the adhesive system. Such energy may include thermal energy, e-beam energy, UV light, and the like.

Suitable compatiblized and passivated refectory solid may include a plurality of particles of one or more metal, metalloid, ceramic, or organic material. Refractory may include materials with a high melting temperature, such as melting temperatures in a range of greater than about 1000 degrees Celsius. In one embodiment, the solid may include aluminum, antimony, arsenic, beryllium, boron, carbon, chromium, copper, gallium, gold, germanium, indium, iron, hafnium, magnesium, manganese, molybdenum, phosphorous, silicon, silver, titanium, tungsten, or zirconium, or the like, or an alloy of two or more thereof. In one embodiment, the solid may include one or more of arsenic, aluminum, boron, gallium, germanium, silicon, titanium, or an oxide or nitride thereof, such as alumina, silica, titania, boron nitride, and the like. For ease of reference, silica may be used as a non-limiting example of a suitable solide. Silica may include colloidal silica (CS), fused silica, or fumed silica, and the like.

Prior to compatibilizing and passivating, a suitable solid oxide may have an active surface termination site that comprises a silanol or hydroxyl group. A suitable solid nitride may have the active surface termination site include an amide or an imide. Subesquent to compatibilizing and passivating, the density of active termination sites may be controlled to be in a predetermined range. For example, with colloidal nano-particle silica the active termination site density may be about 5 active sites per square nanometer (OH/nm²) or less, about 4.75 OH/nm² or less, or in a range of from about 5 OH/nm² to about 1 OH/nm², from about 5 OH/nm² to about 3 OH/nm², or from about 4.5 OH/nm² to about 4.0 OH/nm². Because the active termination site density may correspond to shelf life or stability, a suitable stability ratio (the ratio of viscosity (two weeks/initial)), may be less than about 5, less than about 4, less than about 3 less than about 2, or about 1.

As noted hereinabove, compatibilizing and passivating or capping active termination sites may be accomplished by, for example, a sequential treatment. A first portion of active surface termination sites may be reacted with a compatiblizing composition. A suitable compatiblizing composition may include those disclosed hereinabove, such as an alkoxysilane having an organic moiety that may be one or more of acrylate, alkyl, phenyl, cyclohexyloxy, or glycidyl. Of the remaining active termination sites, a second portion may be reacted with a passivating composition, such as a silazane or other capping agent as disclosed herein.

A suitable water dispersion of colloidal silica for use as a precursor to compatiblized and passivated colloidal silica may be commercially obtained from, for example, Nissan Chemical America Corporation (Houston, Tex.) under the tradename SNOWTEX, or NALCO 1034A, which is available from Nalco Chemical Company (Napier, Ill.). SNOWTEX 40 has an average particle size in a range of from about 10 nanometers to about 30 nanometers.

The refectory solid initially may be hydrophilic or somewhat incompatible with an organic or non-polar phase due to the presence of active termination sites on the particle surface. For example, colloidal silica may be hydrophilic due to the presence of silanol groups at the surface. The hydrophilicity may make dispersion in an organic phase problematic or impracticable. Compatiblizing the solid surface may create an organophilic coating on the surface of the solid particles to make the particles dispersible in, or compatible with, an organic phase or a non-polar liquid. Compatiblizing may be accomplished with, for example, a trialkoxy organosilanes (e.g., phenyl trimethoxy silane, glycidoxy propyl trimethoxy silane, and the like). To reduce further the content or density of active termination sites on the surface, the compatiblized refectory solid may be post treated or reacted with a capping agent or a passivating agent. The reaction with the capping agent may form particles with a relatively low content of available hydroxyl or silanol groups. As disclosed above, such functional groups may be referred to as active termination sites.

A compatibilized refectory solid may be further treated or capped with one or more capping agent for passivation. Suitable capping agents may include one or more of a triorganosilane, an organodisilazane, organoalkoxysilane, or an organohalosilane such as organochlorosilane. In one embodiment, the capping agent may include one or more of hexamethyl disilazane (HMDZ), tetramethyl disilazane, divinyl tetramethyl disilazane, diphenyl tetramethyl disilazane, N-(trimethyl silyl) diethylamine, 1-(trimethyl silyl) imidazole, trimethyl chlorosilane, pentamethyl chloro disiloxane, trimethylmethoxysilane and pentamethyl disiloxane, and the like.

An acid, a base, or a condensation catalyst may be used to promote condensation of, for example, silanol groups on a silica particle surface and an alkoxy silane group to compatiblize the silica particle. Suitable condensation catalysts may include organo-titanate and organo-tin compounds such as tetrabutyl titanate, titanium isopropoxy bis (acetyl acetonate), dibutyltin dilaurate, and the like, or combinations of two or more thereof.

The compatiblized and passivated (e.g., capped) particles may have a relatively reduced number and/or density of active termination sites on the particle surface. The reduced number or reduced density may provide a stable dispersion of particles in a curing agent, a curable resin, or a mixture of both curing agent and curable resin. Further, reduced density of active termination sites (e.g., hydroxyl content on compatiblized and passivated silica) may reduce or eliminate reactions with an anhydride, which may otherwise react with, for example, available hydroxyl groups. Such anhydride/hydroxyl reactions may form a free acid. Thus, reducing or eliminating active termination sites, such as by passivation, may reduce or eliminate free acid formation and may increase stability.

The amount of refectory solid present in a cure system may be expressed as a weight percent of the total weight. The refectory solid may be present in a cure system in an amount greater than about 0.5 weight percent, or in a range of from about 0.5 weight percent to about 80 weight percent. In one embodiment, the refectory solid content may be present in a cure system in an amount in a range of from about 1 weight percent to about 5 weight percent, from about 5 weight percent to about 10 weight percent, from about 10 weight percent to about 20 weight percent, from about 20 weight percent to about 30 weight percent, from about 30 weight percent to about 40 weight percent, from about 40 weight percent to about 50 weight percent, from about 50 weight percent to about 60 weight percent, or greater than 60 weight percent.

Suitable refractory solids may have a surface area greater than about 20 square meters per gram, greater than about 60 square meters per gram, or greater than about 150 square meters per gram. The solid may include a plurality of nano-particles having an average diameter in a range of from about 1 nanometer to about 100 nanometers. In one embodiment, the refractory solids may have an average particle size of less than about 1 micrometer to about 500 nanometers, from about 500 nanometers to about 250 nanometers, from about 250 nanometers to about 100 nanometers, from about 100 nanometers to about 50 nanometers, from about 50 nanometers to about 25 nanometers, from about 25 nanometers to about 10 nanometers, from about 10 nanometers to about 5 nanometer, or less than about 5 nanometer.

Suitable particles may have one or more of a spherical, amorphous or geometric morphology. In one embodiment, the particles may be amorphous. Suitable particles may be porous, may be non-porous, or may include some porous and some non-porous particles. The pores may be uniform in shape or size, or may be shaped and/or sized differently from each other.

A suitable low temperature liquid curing agent may include an anhydride, such as carboxylic acid anhydride, with a relatively low melt point (below about 100 degrees Celsius) or that may be liquid at about room temperature. Low temperature may include temperatures in a range of less than about 100 degrees Celsius, and particularly may include temperatures in a range of less than about 50 degrees Celsius. In one embodiment, the curing agent is a flowable liquid in a temperature range of from about 25 degrees Celsius to about 35 degrees Celsius.

Liquid refers to a property of being fluid or able to flow or thermoplastically deform. A measure of fluidity may be expressed as viscosity, which is the degree to which a fluid may resist flow under an applied force, as measured by the tangential friction force per unit area divided by the velocity gradient under conditions of streamline flow. In one embodiment, the cure system at low temperature may have a Brookfield viscosity of less than about 1000 Poise, in a range of from 1000 Poise about to about 100 Poise, from about 100 Poise to about 1000 centipoise, from about 1000 centipoise, or less than about 1000 centipoise. Viscosity may be measured according to ASTM D-2393-67, which is incorporated herein by reference. The viscosity may differ from embodiment to embodiment, for example, in response to changes in filler loading or type, temperature, and selection of curing agent.

Suitable liquid or low melting temperature anhydrides may include one or more aromatic anhydride, aliphatic anhydride, or cycloaliphatic anhydride. The curing agent may include one or more carboxylic acid anhydrides, which may be selected from aromatic carboxylic acid anhydride, aliphatic carboxylic acid anhydride, or cycloaliphatic carboxylic acid anhydride. Carboxylic anhydrides may be prepared by reacting a carboxylic acid with an acyl halide, or by dehydrating a carboxylic acid, that is, eliminate water between two carboxylic acid molecules to form the anhydride. Alternatively, carboxylic acid anhydrides may be obtained commercially from common chemical suppliers.

Aromatic anhydrides may include one or more of benzoic anhydride; phthalic anhydride; 4-nitrophthalic anhydride; naphthalene tetracarboxylic acid dianhydride; naphthalic anhydride; tetrahydro phthalic anhydride; derivatives thereof; and the like. In one embodiment, a curing agent may include one or more aromatic carboxylic acid anhydrides. Cycloaliphatic anhydrides may include one or more of cyclohexane dicarboxylic anhydride, hexahydro phthalic anhydride, methyl-hexahydro phthalic anhydride (MHHPA), derivatives thereof, and the like. In one embodiment, a curing agent may include 5,5′-(1,1,3,3,5,-hexamethyl-1,5-trisiloxane diyl) bis [hexahydro 4,7-methanoisobenzofuran-1,3-dione] (TriSNBA), which is commercially available from GE Silicones (Waterford, N.Y.).

In one embodiment, a curing agent may include one or more of butanoic anhydride; dodecenyl succinic anhydride; 2,2-dimethyl glutaric anhydride; ethanoic anhydride; glutaric anhydride; hexafluoro glutaric acid anhydride; itaconic anhydride; tetrapropenylsuccinic anhydride; maleic anhydride; 2-methyl glutaric anhydride; 2-methyl propionic anhydride 1,2-cyclohexane dicarboxylic anhydride; octadecyl succinic anhydride; 2-or n-octenyl succinic anhydride; 2-phenylglutaric anhydride; propionic acid anhydride; 3,3-tetramethylene glutaric anhydride; derivatives thereof; and the like.

Structures of some other suitable anhydrides are shown below.

The cure system may be blended, dispersed and/or mixed into a curable resin to form an adhesive system. In one embodiment, the resin may have a filler pre-dispersed therein. That is, prior to mixing both the cure system and the resin system each have a high content of refractory solids dispersed therein.

Suitable resins may include one or more aliphatic epoxy resins, cycloaliphatic epoxy resins, or aromatic epoxy resins. Suitable aliphatic epoxy resins may include one or more of butadiene dioxide, dimethyl pentane dioxide, diglycidyl ether, 1,4-butanediol diglycidyl ether, diethylene glycol diglycidyl ether, and dipentene dioxide, and the like. Suitable aliphatic epoxy monomers may include one or more of butadiene dioxide, dimethylpentane dioxide, diglycidyl ether, 1,4-butanediol diglycidyl ether, diethylene glycol diglycidyl ether, or dipentene dioxide, and the like. In one embodiment, the aliphatic dioxirane monomer may include CYRACURE UVR 6105, which is commercially available from Dow Chemical (Midland, Mich.).

Suitable cycloaliphatic epoxy resins may include one or more of 3-cyclohexenyl methyl-3-cyclohexenyl carboxylate diepoxide; 2-(3,4-epoxy) cyclohexyl-5,5-(3,4-epoxy) cyclohexane-m-dioxane; 3,4-epoxy cyclohexyl alkyl-3,4-epoxy cyclohexane carboxylate; 3,4-epoxy-6-methyl cyclohexyl methyl-3,4-epoxy-6-methyl cyclo hexane carboxylate; vinyl cyclohexane dioxide; bis (3,4-epoxy cyclohexyl methyl) adipate; bis (3,4-epoxy-6-methyl cyclohexyl methyl) adipate; bis (2,3-epoxy cyclopentyl) ether; 2,2-bis (4-(2,3-epoxy propoxy) cyclohexyl) propane; 2,6-bis (2,3-epoxy propoxy cyclohexyl-p-dioxane); 2,6-bis (2,3-epoxy propoxy) norbornene; diglycidyl ether of linoleic acid dimer; limonene dioxide; 2,2-bis (3,4-epoxy cyclohexyl) propane; dicyclopentadiene dioxide; 1,2-epoxy-6-(2,3-epoxy propoxy) hexahydro 4,7-methanoindane; p-(2,3-epoxy) cyclopentyl phenyl-2,3-epoxypropyl ether; 1-(2,3-epoxy propoxy) phenyl-5,6-epoxy hexahydro-4,7-methanoindane; (2,3-epoxy) cyclopentyl phenyl-2,3-epoxy propyl ether); 1,2-bis (5-(1,2-epoxy) 4,7-hexahydro methano indanoxyl) ethane; cyclopentenyl phenyl glycidyl ether; cyclohexane diol diglycidyl ether; diglycidyl hexahydrophthalate; and 3-cyclohexenyl methyl-3-cyclohexenyl carboxylate diepoxide; and the like. In one embodiment, a cycloaliphatic epoxy monomer may include one or more 3-cyclohexenyl methyl-3-cyclohexenyl carboxylate diepoxide, 3-(1,2-epoxy ethyl)-7-oxabicycloheptane; hexanedioic acid, bis (7-oxabicyclo heptyl methyl) ester; 2-(7-oxabicyclohept-3-yl)-spiro-(1,3-dioxa-5,3′-(7)-oxabic yclo heptane; and methyl 3,4-epoxy cyclohexane carboxylate, and the like.

Suitable aromatic epoxy resins may include one or more of bisphenol-A epoxy resins, bisphenol-F epoxy resins, phenol novolac epoxy resins, cresol-novolac epoxy resins, biphenol epoxy resins, biphenyl epoxy resins, 4,4′-biphenyl epoxy resins, polyfunctional epoxy resins, divinylbenzene dioxide, resorcinol diglyciyl ether, and 2-glycidyl phenyl glycidyl ether. Other suitable resins may include silicone-epoxy resins and siloxane epoxy resins. Bisphenol-F resins may be commerically available from Resolution Performance Products (Pueblo, Colo.).

Optional additives may be incorporated into the resin portion of the system, the curing agent portion of the system, or both. Suitable additives may include one or more catalyst, accelerator, flexibilizer, carbinol, organic diluent, suspension agent, fire retardant, pigment, thermally conductive filler, electrically conductive filler, thermally insulative filler, electrically insulative filler, and the like.

A suitable catalyst or accelerator may initiate a crosslinking process, accelerate cure rate, or decrease cure time or temperature of an adhesive system. A catalyst or accelerator may be present in an amount less than about 10 parts per million (ppm), in a range of from about 10 ppm to about 100 ppm, from about 100 ppm to about 0.1 weight percent, from about 0.1 weight percent to about 1 weight percent, or greater than about 1 weight percent of the total formulation weight.

A suitable catalyst or an accelerator may include, but is not limited to, an onium catalyst or a free-radical generating compound. Suitable onium catalysts may include bisaryliodonium salts (e.g. bis (dodecyl phenyl) iodonium hexafluoro antimonate, (octyl oxyphenyl phenyl) iodonium hexafluoro antimonate, bisaryl iodonium tetrakis (penta fluorophenyl) borate), triaryl sulphonium salts, and combinations of two or more thereof. Suitable free-radical generating compounds may include one or more aromatic pinacols, benzoinalkyl ethers, organic peroxides, and the like. The presence of a free radical generating compound may enable decomposition of an onium salt at a relatively lower temperature.

In one embodiment, a catalyst or an accelerator may be added to an epoxy-based adhesive system. Useful catalysts or accelerators may include one or more amine; alkyl-substituted imidazole; imidazolium salt; phosphine; metal salt, such as aluminum acetyl acetonate (Al(AcAc)₃); salt of nitrogen-containing compound; and the like. The nitrogen-containing compound may include, for example, one or more amine compounds, di-aza compounds, tri-aza compounds, polyamine compounds and the like. A salt of a nitrogen-containing compound may include, for example 1,8-diazabicyclo (5,4,0)-7-undecane. The salt of the nitrogen-containing compounds may be obtained commercially, for example, as POLYCAT SA-1 or POLYCAT SA-102. POLYCAT SA-1 is a delayed-action, heat-activated catalyst based on the cyclic amine, 1,8 diaza-bicyclo (5,4,0) undec-ene-7. POLYCAT SA-1 contains DBU catalyst and an organic acid “blocker”. POLYCAT is a trademark of Air Products and Chemicals, Inc (Allentown, Pa.). Other suitable catalysts may include triphenyl phosphine (TPP), N-methylimidazole (NMI), and/or dibutyl tin dilaurate (DiButSn).

Additives, such as flexibilizers, may include one or more organic compounds having a hydroxyl-containing moiety. Suitable flexibilizers may include one or more of polyol or bisphenol. The polyol may be straight chain, branched, cycloaliphatic, or aromatic and may contain from about 2 to about 100 carbon atoms. Examples of such polyfunctional alcohols may include one or more of ethylene glycol; propylene glycol; 2,2-dimethyl-1,3-propane diol; 2-ethyl, 2-methyl, 1,3-propane diol; 1,3-pentane diol; 1,5-pentane diol; dipropylene glycol; 2-methyl-1,5-pentane diol; 1,6-hexane diol; dimethanol decalin, dimethanol bicyclo octane; 1,4-cyclohexane dimethanol; triethylene glycol; and 1,10-decane diol. In one embodiment, an alcohol may include 3-ethyl-3-hydroxymethyl oxetane (commercially available as UVR6000 from Dow Chemicals (Midland, Mich.)).

Suitable bisphenols may include one or more dihydroxy-substituted aromatic hydrocarbon. In one embodiment, a dihydroxy-substituted aromatic compound may include one or more of 4,4′-(3,3,5-trimethyl cyclohexylidene)-diphenol; 2,2-bis(4-hydroxyphenyl) propane (bisphenol A); 2,2-bis(4-hydroxyphenyl) methane (bisphenol F); 2,2-bis (4-hydroxyl-3,5-dimethylphenyl) propane; 2,4′-dihydroxy diphenylmethane; bis(2-hydroxyphenyl) methane; bis(4-hydroxyphenyl) methane; bis (4-hydroxyl-5-nitrophenyl)methane; bis(4-hydroxyl-2,6-dimethyl-3-methoxyphenyl) methane; 1,1-bis(4-hydroxyphenyl)ethane; 1,1-bis (4-hydroxyl-2-chlorophenyl ethane; 2,2-bis(3-phenyl-4-hydroxyphenyl) propane; bis(4-hydroxyphenyl)cyclohexyl methane; 2,2-bis(4-hydroxyphenyl)-1-phenylpropane; 2,2,2′,2′-tetrahydro-3,3,3′,3′-tetramethyl,1′-spir obi {1H-indene}-6,6′-diol (SBI); 2,2-bis(4-hydroxyl-3-methylphenyl)propane (DMBPC); and C1-C13 alkyl-substituted resorcinols, and the like.

A suitable organic diluent may be added to an adhesive system according to embodiments of the invention. The organic diluent may decrease a viscosity of the adhesive system. Suitable reactive diluents may include, but are not limited to, dodecylglycidyl ether, 4-vinyl-1-cyclohexane diepoxide, and di (beta-(3,4-epoxy cyclohexyl) ethyl) tetramethyl disiloxane, or combinations of two or more thereof. Other diluents may include monofunctional epoxies and/or compounds containing at least one epoxy functionality. Such diluents may include, but are not limited to, alkyl derivatives of phenol glycidyl ethers such as 3-(2-nonylphenyloxy)-1,2-epoxy propane or 3-(4-nonylphenyloxy) 1,2-epoxy propane; glycidyl ethers of phenol; substituted phenols such as 2-methylphenol, 4-methyl phenol, 3-methylphenol, 2-butylphenol, 4-butylphenol, 3-octylphenol, 4-octylphenol, 4-t-butylphenol, 4-phenylphenol, and 4-(phenyl isopropylidene)phenol; and the like. In one embodiment, the reactive diluent may include 3-ethyl-3-hydroxymethyl-oxetane, which is commercially available as UVR6000 from Dow Chemical (Midland, Mich.).

A suitable flame retardant may include one or more material that contains phosphorus, iron, halogen, oxide, or hydroxide. In one embodiment, a flame retardant additive may include phosphoramide, triphenyl phosphate (TPP), resorcinol diphosphate (RDP), bisphenol A disphosphate (BPA-DP), organic phosphine oxide, halogenated resin (e.g., tetrabromobisphenol A), metal oxide (e.g. bismuth oxide), metal hydroxide (e.g., MgOH), and combinations of two or more thereof. Suitable pigment may include one or both of reactive and non-reactive materials.

In one embodiment, a cure system may be produced by dispersion of refractory solids (e.g. CS) into a liquid curing agent and a solvent to form a solution. A suitable solvent may include a hydroxyl-group free solvent, such as propylene glycol methyl ether acetate, toluene, xylene, supercritical fluid (e.g., SCF CO₂), and the like.

After the dispersion or mixing, the solvent may be removed. Suitable solvent removal methods may include affecting the temperature and/or pressure to volatilize the solvent. That is, heat, vacuum, or both may be used to extract or remove the solvent from the dispersion. If a supercritical fluid, such as supercritical carbon dioxide, is used, room temperature and pressure may be sufficient to remove the solvent. Subsequently, a solvent-free filled low temperature liquid cure system according to an embodiment of the invention may be recovered and stored.

In one embodiment, a cure system further may be mixed with a curable resin to form an adhesive system. The resulting adhesive system may have a flowable or workable viscosity for a predetermined time, i.e., pot life. For a no-flow underfill application, the viscosity may be such to allow flow of the underfill during dispensing on the substrate and formation of solder electrical connection during a reflow process. Viscosity selection may be made by one or more of determining amounts of refractory solids in the resin, amounts of refractory solids in the cure system, the initial unfilled viscosity of the resin and/or cure system, temperature, the presence or amount of additives or flow-modifiers, control over working pressure, use of sonic vibrations, and the like.

The adhesive system according to embodiments of the invention may be used in an electronic device. In one embodiment, the adhesive system may be used as an underfill material, such as a no-flow underfill, in a flip chip assembly to secure a chip to a substrate. The adhesive system may exhibit one or more of: prolonged room temperature stability, desirable solder ball fluxing, and a coefficient of thermal expansion below about 50 ppm/° C. when cured and used as, for example, an encapsulant or an underfill. In one embodiment, a cured adhesive system may have properties that include one or more of a low CTE (below about 40 ppm/° C.), self-fluxing properties during application, a high Tg (above about 100 degrees Celsius), a high heat deflection temperature (HDT), and relatively high optical transparency.

An embodiment of the invention may provide a no-flow underfill material having a coefficient of thermal expansion, when cured, of less than 50 ppm/° C., in a range of from about 50 ppm/° C. to about 40 ppm/° C., from about 40 ppm/° C. to about 30 ppm/° C., or less than about 30 ppm/° C. An embodiment may enable a final filler loading of greater than 30 weight percent, a range of from about 30 weight percent to about 40 weight percent, from about 40 weight percent to about 50 weight percent, or greater than about 50 weight percent, while maintaining one or more of an acceptable level of processability, transparency, or a desirably high glass transition temperature (Tg). Processability relates to properties that may include flowability, viscosity, visco-elasticity, tack, wetability, out-gassing, percent void, shelf life, cure time, cure temperature, and the like. Transparency relates to the property of permitting the relatively free passage of electromagnetic radiation through a pre-determined thickness of material without one or more refraction, reflection or absorption. Glass transition temperature relates to an inflection point on a plot of modulus versus temperature. The Tg indicates a temperature range above which a material may undergo plastic deformation, or may change from a rigid or brittle state to a rubbery or softened state.

In one embodiment, an adhesive system may be a no-flow underfill, a capillary flow underfill, a wafer level underfill, a thermal interface material (TIM), and/or pre-applied and optionally B-staged on a substrate, and may be dispensable and have utility in the fabrication of an electronic device, such as a computer, an optical device, or a semiconductor assembly. As an underfill material or encapsulant, the adhesive system may reinforce physical, mechanical, and electrical properties of solder bumps that may secure a chip to a substrate, and/or may act as flux during solder bump melting.

No-flow underfilling may include dispensing an underfill encapsulant material on the substrate or semiconductor device and performing solder bump reflowing simultaneously with underfill encapsulant curing. Wafer level underfilling may include dispensing underfill materials onto the wafer before dicing into individual chips that are subsequently mounted in the final structure via flip-chip type operations. Alternatively to no-flow underfill, dispensing the underfill material may include applying in a fillet or bead extending along at least one edge of a chip, and allowing the underfill material to flow by capillary action under the chip to fill all, or nearly all, gaps between the chip and the substrate.

In one embodiment, an adhesive according to embodiments of the invention may be energy cured, such as by heat, UV light, microwave energy, electron been energy, and the like. For heat or thermal curing, a suitable temperature may be in a range of from about 50 degrees Celsius to about 100 degrees Celsius, from about 100 degrees Celsius to about 200 degrees Celsius, from about 200 degrees Celsius to about 250 degrees Celsius, or greater than about 250 degrees Celsius. For no flow underfill, the cure temperature is in a range of from about 183 degrees Celsius (melting point of eutectic solder) to about 230 degrees Celsius for Sn/Pb eutectic solder and from about 230 degrees Celsius to about 260 degrees Celsius for lead-free solder. Curing may occur over a period of less than about 30 seconds, in a range between about 30 seconds and about 1 minute, from about 1 minute to about 5 minutes, from about 5 minutes to about 30 minutes, from about 30 minutes to about 1 hour, from about 1 hour to about 5 hours, or greater than about 5 hours. For no flow underfill a cure process (during a reflow) may be in a range of from about 3 minutes to about 10 minutes.

Optional post-curing may be performed at a temperature of less than 100 degrees Celsius, in a range of from about 100 degrees Celsius to about 150 degrees Celsius, or greater than about 150 degrees Celsius, over a period of less than one hour, in a range of from about 1 hour to about 4 hours, or greater than about 4 hours. For no-flow underfill, the post cure may be at a temperature in a range of from about 100 degrees Celsius to about 160 degrees Celsius over a period of from about 1 to about 4 hours. Other times, temperatures and pressures for curing and post-curing may be selected with reference to application specific parameters.

In one embodiment, a cure system according to an embodiment of the invention may consist essentially of a liquid curing agent and compatiblized and passivated silica. In another embodiment, a cure system may consist essentially of a liquid carboxylic acid anhydride curing agent, and compatiblized colloidal silica treated with a capping agent. In yet another embodiment, a cure system may consist essentially of a room temperature liquid anhydride-curing agent, and compatiblized and passivated colloidal silica having a nano-size average particle diameter.

EXAMPLES

The following examples are intended only to illustrate methods and embodiments in accordance with the invention, and as such should not be construed as imposing limitations upon the claims. Unless specified otherwise, all ingredients are commercially available from such common chemical suppliers as Alpha Aesar, Inc. (Ward Hill, Mass.), Sigma-Aldrich Corp. (St. Louis, Mo.), and the like.

Example 1

Preparation of Compatiblized and Passivated Solids

A mixture is made by adding 300 grams of SNOWTEX-ZL (80 nm average particle size) to 300 grams of isopropyl alcohol (IPA). After thoroughly mixing, 2 grams of phenyl trimethoxysilane (Ph(OMe)₃Si) is added to the mixture. The resulting mixture is refluxed for three hours. After reflux, the mixture is cooled to room temperature. The cooled mixture has 600 grams of methoxypropanol added while mixing, until thoroughly mixed. A stripping process removes 600 grams of volatile material, by weight. Hexamethyl disilazane (HMDZ) is added to the stripped mixture in an amount of 6 grams. The mixture is thoroughly mixed, refluxed for 1 hour at elevated temperature, and then stripped to 200 grams total weight. 300 grams of propylene glycol methyl ether acetate or 1-methoxy-2-acetoxypropane (PGMEA) is added and mixed thoroughly. The resulting mixture is stripped of 300 grams of volatile weight and filtered. The yield is 250 grams of compatiblized and passivated colloidal silica material having solids of 29.10 weight percent. The recovered sample is labeled Sample 1A. An ingredient list is shown in Table 1, below. The above disclosed process is repeated to form Sample 1B, the difference being that silica having an average particle size of 50 nm, rather than 80 nm, is used.

< /tr>

TABLE 1
Ingredient list for compatiblized
and passivated solids (Sample 1A)
	INGREDIENT	AMOUNT (g)
	Snowtex-ZL	300
	Snowtex-ZL 80 nm particles,
	Conc. OH = 5/nm2
	IPA	300
	Ph(OMe)3Si	2
	Methoxypropanol	600
	HMDZ	6
	PGMEA	300
	Yield	215
	Solids	29.10%
	Appearance	white liquid

Example 2 through Example 4

Preparation of Cure System Including Compatiblized and Passivated Solids

The compatiblized and passivated colloidal silica materials produced in Example 1 (Samples 1A and 1B) are added to liquid anhydride materials methylhexahydrophthalic anhydride (MHHPA) and 5,5′-(1,1,3,3,5,-hexamethyl-1,5-trisiloxane diyl) bis [hexahydro-4,7-methanoisobenzofuran-1,3-dione] (TriSNBA) to form Samples 2-4. Samples 2-4 were evaporated using a commercially available rotary evaporator at 70 degrees Celsius. Rotary evaporators may be obtained from, for example, Thomas Industries, Inc. (Skokie, Ill.). An ingredient list for the cure systems containing compatiblized and passivated silica is shown in Table 2. A list of properties for the Samples 2-4 shown in Table 2 is shown is Table 3. The viscosity measurements are performed with SP # 40 at 10 rpm, and the results are in centipoise, unless otherwise indicated.

TABLE 2
Ingredient list for cure systems containing Samples 1A and 1B).
	Sample 2	Sample 3	Sample 4
	Sample 1A	35	35	—
	( 80 nm ave size)
	Sample 1B	—	—	37.3
(50 nm ave size)
	MHHPA	10	—	10
	TrisNBA/MHHPA	—	10	—
	(40/60 ratio)

< tr>

TABLE 3
Properties for cure systems (Samples 2-3)
that contain Samples 1A and 1B.
	Sample 2	Sample 3	Sample 4
Appearance	yellow	yello w	light yellow
Mass	20.15	20.06	20.1
% solids	50	50	50
Vis cosity (centipoise)	600	3040	920

Example 5 and Example 6

Preparation of Adhesive Systems that Include a Cure System

An aliphatic dioxirane monomer, CYRACURE UVR 6105 is blended with Bisphenol F epoxy resin in a 75/25 ratio to form a base resin. A reactive diluent, UVR6000, is added to the base resin to form a mixture. A cure catalyst, POLYCAT SA-1, is added to the mixture of base resin and diluent to form a catalyzed mixture. The catalyzed mixture is blended with 60 weight percent of a cure system (Samples 2 or 3) at room temperature for approximately 10 minutes to form an adhesive system (Samples 5 and 6, respectively). After which, each adhesive system (Samples 5 and 6) is degassed at relatively high vacuum at room temperature for 20 minutes. Samples 5 and 6 are stored at negative 40 degrees Celsius.

For test and evaluation, Samples 5 and 6 are applied to a chip and to a substrate. The chip and substrate are set together to form an assembly. Thermal energy is applied to cure the adhesive systems, Samples 5 and 6. Test results are listed in Table 5. Viscosity is performed with spindle #40 at 20 rpm at room temperature, the results are in centipoise.

TABLE 4
Ingredient list for adhesive systems (Sample 5 and Sample
6) that each include a curable resin and a cure system.
	INGREDIENT	Sample 5	Sample 6
	Base Resin 1	5	5
	Sample 2	4.07	—
	Sample 3	—	5
	UV R6000	0.2	0.2
	Polycat SA-1	0.0188	0.0216

TABLE 5
Properties list for adhesive systems.
	Test	Sample 5	Sample 6
	Fluxing of eutectic solder	Good	Good
	Visco sity (centipoise)	4880	29700
	% solids	53%	52%
	Tg TMA (° C.)	138.0	154.0
	CTE-20 -80 (ppm/° C.)	36.0	39.0
	DS C peak (° C.)	214.4	208.1
	DSC H onset (° C.)	164.4	154.7
	DSC H (J/g)	199.0	168.8
	DSC Tg (° C.)	123.5	147.0

The foregoing examples are merely illustrative, serving to illustrate only some of the features of the invention. The appended claims are intended to claim the invention as broadly as it has been conceived and the examples herein presented are illustrative of selected embodiments from a manifold of all possible embodiments. Accordingly it is Applicants' intention that the appended claims are not to be limited by the choice of examples utilized to illustrate features of the present invention. As used in the claims, the word “comprises” and its grammatical variants logically also subtend and include phrases of varying and differing extent such as for example, but not limited thereto, “consisting essentially of” and “consisting of.” Where necessary, ranges have been supplied, those ranges are inclusive of all sub-ranges there between. It is to be expected that variations in these ranges will suggest themselves to a practitioner having ordinary skill in the art and where not already dedicated to the public, those variations should where possible be construed to be covered by the appended claims. It is also anticipated that advances in science and technology will make equivalents and substitutions possible that are not now contemplated by reason of the imprecision of language and these variations should also be construed where possible to be covered by the appended claims.